TECHNIPOL® PA 2202

TECHNIPOL® PA 2202

DESCRIPTION

Technipol® PA 2202 is a thermoplastic adhesive co-polyamide based for the automotive filter industry. It is characterized by a quick setting time, a good flexibility, a good wettability and a good chemical resistance.
Application via extruder is recommended.

Technipol® PA 2202 contains around 80% of raw materials coming from renewable resources (non-edible).

TECHNICAL CHARACTERISTICS

Properties

Test method

U.M.

Values

Colour

   

Amber

Density

ASTM D 792 / ISO 1183

g/cm3

0,98

Softening point

ASTM D 3461

°C

205

Brookfield viscosity* (220 °C)

MI 12

Pa·s

9,5

Hardness (15 s)

ASTM D 2240 / ISO 868

Shore D

35

Strength at break

ASTM D 638 / ISO 527

MPa

7

Elongation at break

ASTM D 638 / ISO 527

%

460

* Cone/ plate Viscometer, Model Brookfield CAP 2000+

VISCOSITY vs TEMPERATURE CURVE

APPLICATION INDICATIONS

Suggested temperature profile* for extrusion:

UNDER HOPPER

FEEDING ZONE

COMPRESSION

ZONE

METERING ZONE

EXTRUSION DIE/ HOSE

NOZZLE

50° – 70°C

150° – 170°C

175° – 190°C

200° - 210°C

210° - 220°C

230° - 250°C

Suggested temperature profile* for melters:

PRE-HEATING GRILLS

TANK

HOSE

NOZZLE

180° – 195 °C

220° – 240 °C

230° – 240 °C

230° – 250 °C

* depending on the substrate and the applicator

PACKAGING

25 kg bags equipped with an aluminum film barrier against moisture action.
500 kg cardboard octabins equipped with an inner PE liner.
500 kg big bags.

STORAGE

Product is stable for 12 months when stored unopened in its original packaging, kept in a cool and dry place and protected from light. When stocked around 5 – 10°C or below, it is recommended to keep it at 15 – 20°C for at least for 24 hours before using it.

  • Scheda Tecnica: